| ECO |
HYDRINâ |
POLYEPICHLOROHYDRIN ELASTOMERS |
|
CO/ECO/ETER | |
|
Grade |
Chlorine content % by weight |
Mooney Viscosity ML 1+4 @ 100°C |
Specific Gravity g/cm3 |
Tg
oC |
Main characteristics &
applications |
|
Hydrinâ
H-45
|
36 |
40-50 |
1,37 |
-21 |
Homopolymer.
Outstanding ozone and gas permeation resistance. Used
for fuel hose, vibration mounts,
adhesives and gaskets |
|
Hydrinâ
H-55
|
36 |
50-60 |
1,37 |
-21 |
|
Hydrinâ
H-65
|
36 |
60-70 |
1,37 |
-21 |
|
![]()
|
|
Hydrinâ
H1100
|
35 |
48-68 |
1,35 |
-25 |
Special copolymer. Gives improved ozone
resistance and can be sulphur or peroxide
cured. |
|
![]()
|
|
Hydrinâ
C2000
|
26 |
90-102 |
1,28 |
-38 |
Copolymer. |
|
Hydrinâ
C2000L
|
26 |
65-75 |
1,28 |
-38 |
|
Hydrinâ
C2000LL
|
26 |
53-65 |
1,28 |
-38 |
Copolymer grades with
low viscosity. |
|
Hydrinâ
C2000XL
|
26 |
40-52 |
1,28 |
-38 |
|
![]()
|
|
Hydrinâ
T3000
|
24,7 |
80-94 |
1,28 |
-42 |
Terpolymer. Sulphur or peroxide
curable, can be blended with almost all other
elastomers. |
|
Hydrinâ
T3000L
|
24,7 |
65-79 |
1,28 |
-42 |
|
Hydrinâ
T3000LL
|
24,7 |
50-64 |
1,28 |
-42 |
|
![]()
|
|
Hydrinâ
T3100
|
29 |
63-77 |
1,30 |
-36 |
Terpolymer. Higher ECH and AGE content
compared to Hydrin T, can be sulphur or peroxide cured |
|
Hydrinâ
T3102
|
29 |
80-100 |
1,30 |
-37 |
|
Hydrinâ
T3105
|
28 |
70-80 |
1,28 |
-37 |
|
![]()
|
|
Hydrinâ
T3106
|
21 |
53-67 |
1,28 |
-48 |
Terpolymer. Excellent low temperature
flexibility. | | |
|
|
|
|
|
|
|
|
|
|
|