| HNBR |
ZETPOL |
HYDROGENATED NITRILE RUBBERS |
| | |
| Grade |
Bound Acrylonitrile % by weight |
Mooney Viscosity ML 1+4 @ 100°C |
Specific Gravity g/cm3 |
Iodine value g/100g |
Main characteristics &
applications |
|
Zetpol
00201,2
|
49 |
56-76 |
1,00 |
22 |
Maximum fuel and solvent resistance.
Especially designed for flex fuels. |
|
![]()
|
|
Zetpol
1000L1,2
|
44,2 |
63-77 |
0,98 |
max. 7 |
Maximum
fuel and heat resistance. |
|
Zetpol
10101,2
|
44 |
79-92 |
0,98 |
10 |
Excellent fuel and solvent resistance
for fuel line hoses, diaphragms, in-tank isolators,
refrigerant hoses, gaskets and
O-rings. |
|
Zetpol
1020L2
|
44 |
48-68 |
0,98 |
25 |
|
Zetpol
10201,2
|
44 |
71-85 |
0,98 |
25 |
|
![]()
|
|
Zetpol
14102
|
43,2 |
50-90 |
0,98 |
10 |
Excellent heat resistance in gasoline and RME.
Suitable for peroxide curing. |
|
Zetpol
14201,2
|
43,2 |
50-90 |
0,98 |
24 |
Similar to Zetpol 1410. Suitable for sulfure and
peroxide curing. |
|
![]()
|
|
Zetpol
20001,2
|
36 |
78-92 |
0,95 |
max. 7 |
Maximum heat and chemical resistance
for O-rings, seals, gaskets and hoses for both automotive
and oilfield components. |
|
Zetpol
2000L1,2
|
36 |
58-72 |
0,95 |
max. 7 |
|
Zetpol
20101,2
|
36 |
78-92 |
0,95 |
11 |
Excellent heat, oil and chemical
resistance for O-rings, seals, gaskets and hoses for
automotive and energy industries. Low viscosity for
improved flow, high viscosity for high pressure
extrusion resistance |
|
Zetpol
2010L1,2
|
36 |
50-65 |
0,95 |
11 |
|
Zetpol
2010H1,2
|
36 |
min. 120 |
0,95 |
11 |
|
Zetpol
20111,2
|
36 |
75-85 |
0,95 |
18 |
Sulphur and peroxide curable, good
balance of chemical resistance, cold flexibility and
dynamic properties.
Used for timing belts, poly-V-belts. |
|
Zetpol
2011L1,2
|
36 |
52-63 |
0,95 |
18 |
|
Zetpol
20201,2
|
36 |
71-85 |
0,95 |
28 |
Sulphur and peroxide curable for
excellent dynamic characteristics. Uses
are timing and multi-V belts, rolls, hoses,
seals |
|
Zetpol
2020L1,2
|
36 |
50-65 |
0,95 |
28 |
|
Zetpol
20211,2
|
36 |
71-85 |
0,95 |
21 |
Sulphur and peroxide curable, improved
heat resistance, improved dynamic properties. Used for timing belts,
poly-V-belts. |
|
Zetpol
2021L1,2
|
36,2 |
max. 70,5 |
0,95 |
21 |
|
Zetpol
2030L1,2
|
36 |
50-65 |
0,95 |
57 |
Highest unsaturation for superior dynamics for
rolls, belts. |
|
![]()
|
|
Zetpol 3110
|
25 |
85-105 |
0,97 |
15 |
Improved low temperature resistance.
TR 10 of -30°C for HNBR providing a good balance of oil
and low temperature resistance plus improved high
temperature capabilities. |
|
Zetpol 3120
|
25 |
85-100 |
0,97 |
28 |
|
![]()
|
|
Zetpol 3310
|
23,6 |
60-100 |
0,97 |
15 |
Improved low temperature flexibility, increase in
mechanical properties after aging, and volume swell
reduction. |
|
![]()
|
|
Zetpol 4300
|
18,6 |
55-95 |
0,98 |
10 |
Excellent balance of low temperature flexibility
and heat and oil resistance. |
|
![]()
|
|
Zetpol 4310
|
18,6 |
60-100 |
0,98 |
15 |
Excellent balance of low temperature flexibility
and heat and oil resistance. For arctic oil field
applications and automotive uses. |
|
![]()
|
|
Zetpol 4320
|
18,6 |
55-85 |
0,98 |
27 |
Similar to Zetpol 4310,TR10 of
–37°C. | |
|
|
|
|
|
| HNBR |
ZEOFORTE |
MODIFIED
HYDROGENATED NITRILE RUBBERS |
| | |
| Grade
______________ |
Bound Acrylonitrile % by
weight |
Mooney Viscosity ML 1+4 @
100°C |
Specific Gravity
g/cm3 |
Iodine value g/100g |
Main
characteristics & applications |
|
Zeoforte ZSC 2095
|
361 |
83-103 |
1,24 |
41 |
Highly saturated Zetpol modified with ZnO and
methacrylic acid, outstanding mechanical properties at high hardness. |
|
Zeoforte ZSC 2195H
|
361 |
70-902 |
1,24 |
111 |
|
Zeoforte ZSC 2195LCX
|
36,21 |
55-90 |
1,24 |
8,0-14,01 |
|
![]()
|
|
Zeoforte ZSC 2295 N
|
361 |
80-110 |
1,17 |
281 |
Zetpol modified with ZnO and methacrylic acid, new
grades with high dimensional stability and low heat-build-up,
excellent tear resistance, abrasion resistance and good
elongation at high hardness, excellent dynamic properties,
used for timing belts, poly-V-belts and printing rolls.
|
|
Zeoforte ZSC 2295 L
|
36,21 |
60-100 |
1,17 |
23,2-32,81 |
|
Zeoforte ZSC 2295CX
|
361 |
75-110 |
1,17 |
281 |
|
Zeoforte ZSC 2298 L
|
361 |
60-90 |
1,28 |
281 |
|
![]()
|
|
Zeoforte ZSC 2395
|
361 |
60-80 |
1,24 |
561 |
Low
saturated Zetpol modified with ZnO and methacrylic acid, very
good compression set, outstanding dynamical properties, for
paper and steel rolls. |
|
![]()
|
|
Zeoforte ZSC 3195CX
|
23,61 |
70-100 |
1,25 |
10-201 |
Cold
flexible Zetpol modified with ZnO and methacrylic
acid. |
|
![]()
|
|
Zeoforte ZSC 4195CX
|
18,61 |
60-100 |
1,25 |
10-201 |
Cold
flexible Zetpol modified with ZnO and methacrylic
acid. | |
|
|
|
| HNBR/PVC |
ZETPOL |
HYDROGENATED
NBR/PVC POLYBLENDS |
| | |
| Grade
______________ |
Bound Acrylonitrile % by
weight |
Mooney Viscosity ML 1+4 @
100°C |
Specific Gravity
g/cm3 |
Iodine value g/100g |
Main
characteristics & applications |
|
Zetpol PBZ-123
|
441 |
38-582 |
1,08 |
251 |
70:30
HNBR/PVC for ozone, heat and sour gas
resistance. | |
|
|
|
|