| COP |
ZEONOR |
CYCLO
OLEFIN POLYMERS |
| | |
| Properties__ |
Unit |
Measurement methods |
Zeonor 750R
|
Zeonor 1020R
|
Zeonor 1060R
|
Zeonor 1420R
|
Zeonor
1600
|
| Specific
gravity |
- |
ASTM D792 |
1,01 |
1,01 |
1,01 |
1,01 |
1,01 |
| Water
absorption |
- |
ASTM D570 |
<0.01 |
<0.01 |
<0.01 |
<0.01 |
<0.01 |
| Moisture
permeability |
g/m2.24hr |
JIS Z 0280 (300μM) |
0,30 |
0,29 |
0,29 |
0,30 |
- |
| Light
transmittance |
% |
ASTM D1003 (3mm) |
92 |
92 |
92 |
92 |
92 |
| Glass
transition temperature |
oC |
DSC |
70 |
105 |
100 |
136 |
163 |
| Heat
distortion temperature |
oC |
ASTM D648 (18.6kgf) |
68 |
101 |
99 |
136 |
161 |
| Thermal decomposition temperature |
oC |
- |
420 |
420 |
420 |
420 |
420 |
| Linear
expansion coefficient |
cm/cmoC |
ASTM D696 |
7x10-5 |
7x10-5 |
7x10-5 |
7x10-5 |
6x10-5 |
| Melt
flow rate |
g/10min |
JIS K6719 (280oC) |
35 |
20 |
60 |
20 |
7 |
| Mold
shrinkage |
% |
ASTM D955 |
0.1-0.3 |
0.1-0.3 |
0.1-0.3 |
0.5-0.7 |
0.3-0.6 |
| Flexural
modulus |
MPa |
ASTM D790 |
1900 |
2100 |
2100 |
2200 |
2600 |
| Flexural
strength |
MPa |
ASTM D790 |
65 |
80 |
76 |
94 |
119 |
| Tensile
strength |
MPa |
ASTM D638 |
53 |
53 |
53 |
61 |
73 |
| Tensile
modulus |
MPa |
ASTM D638 |
1700 |
2200 |
2100 |
2400 |
2700 |
| Tensile
elongation |
% |
ASTM D638 |
100 |
90 |
60 |
20 |
10 |
| Izod
impact strength |
KJ/m2 |
ASTM D256 |
9 |
6 |
2 |
3 |
3 |
| Dupont
impact strength |
J |
ASTM D256 |
35 |
36 |
26 |
16 |
1 |
| Rockwell
hardness |
- |
ASTM D785 |
- |
20 |
20 |
50 |
75 |
| Volume
resistivity |
Ωm |
ASTM D257 |
>1016 |
>1016 |
>1016 |
>1016 |
>1016 |
| Dielectric
breakdown strength |
KV/mm |
ASTM D149 |
>70 |
>70 |
>70 |
>70 |
>70 |
| Dielectric
constant |
- |
ASTM D150 (1MHz) |
2,3 |
2,3 |
2,3 |
2,3 |
2,3 |
| Dielectric
loss tangent |
- |
ASTM D150 (1MHz) |
0,0002 |
0,0002 |
0,0002 |
0,0002 |
0,0002 |
| UL
flammability rating |
Class |
UL-94 |
(94HB) |
94HB |
94HB |
94HB |
94HB |
| Processability |
|
|
Calendering
Extrusion Injection Moulding |
Calendering
Extrusion Injection Moulding |
Injection
Moulding |
Extrusion
Injection Moulding |
Extrusion | | |
|
|
|
|
|
|
| ZEONOR / ZEONEX |
|
| Chemical
resistance | |
| Marginal
stress |
|
|
|
140kgf/cm2
or more |
|
(usable) |
|
100
to 140kgf/cm2 |
|
(exercise
caution in use) |
|
100kgf/cm2
or less |
|
(unusable) | |
|
Alcohol |
Methanol |
|
|
Ethanol |
|
|
IPA
(isopropyl alcohol) |
|
|
Ketone |
Acetone |
|
|
MEK
(methyl ethyl ketone) |
|
|
Cyclohexanone |
|
|
Ether |
Ethyl
ether |
|
|
THF
(tetrahydrofuran) |
|
|
Aromatic |
Xylene |
|
|
Hydrocarbon |
n-Pentane |
|
|
n-Hexane |
|
|
Chlorohydrocarbon |
1,2-Dichloroethane |
|
|
Other
solvents |
DOP
(dioctylphthalate) |
|
|
DMF
(dimethylformamide) |
|
|
Methyl
cellosolve |
|
|
Limonene |
|
|
Acid |
Hydrochloric
acid (10%) |
|
|
Concentrated
hydrochloric acid |
|
|
Sulfuric
acid (10%) |
|
|
Concentrated
sulfuric acid |
|
|
Acetic
acid (10%) |
|
|
Formic
acid (10%) |
|
|
Nitric
acid |
|
|
Phosphoric
acid |
|
|
nitric
acid (42%), pure water (51%) |
|
|
Base |
Caustic
soda (50%) |
|
|
Aqueous
ammonia (10%) |
|
|
Other
chemicals |
Formaldehyde
(40%) |
|
|
Hydrogen
peroxide water (30%) |
|
|
Foods |
Salad
oil |
|
|
Margarine |
|
|
Lemon
juice |
|
|
Cosmetics |
Hair
liquid |
|
|
Hair
tonic |
|
|
Detergent |
Hair
shampoo |
|
|
Hair
rinse |
| |
|
|
|
|
|
|
|
|
|
|
|